Kerox - HS 98 X10 mm zirconium disc
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental zirconium discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard snterization can be u ...
Kerox - HT 98 X16 mm zirconium disc Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Advantages:
Extraordinary aesthetic parameters Highest level
...
Kerox - HT 98 X16 mm zirconium disc Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Advantages:
Extraordinary aesthetic parameters Highest level
...Kerox - HTML Zirconium Disc 98x14 mm
Characteristics :
Kerox - HT Myltilayer zirconium disc
Features: 
& nbsp & nbsp multi-layer zirconium disc with high translucency. & nbsp & nbsp 6 layers of natural gradient from neck to incisal & nbsp & nbsp high translucency for natural aesthetics & nbsp & nbsp high mechanical strength & nbsp & nbsp perfect contraction & nbsp & nbsp compatible with most Cad / Cam systems
Application: & nbsp & nbsp full-contour crowns
487.04zł +vat
526.00zł
Kerox - zircon disc HS 98 X16 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental Zirconium Discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard sintering can be used ...
Kerox - zirconium disc HS 98 X12 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental zirconium discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard sintering can be used ...
Kerox - zirconium disc HS 98 X14 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental Zirconium Discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard sintering can be used ...
Kerox - zirconium disc HS 98 X18 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental zirconium discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard snterization can be u ...
Kerox - zirconium disc HS 98 X25 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
HS Kerox Dental zirconium discs have the highest flexural strength on the market. A thin layer of zirconium additionally strengthens the prosthetic abutment and masks its metallic color.
Advantages:
- Unique aesthetic qualities
- High level of translucency
- Standard snterization can be u ...
Kerox- HT zirconium disc 98x10 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Advantages:
- Extraordinary aesthetic parameters
Kerox- PMMA CAST disc for Clear casting 98x20 mm
PMMA Castable discs are a material to be used in the technique of combining CAD / CAM technology and classic casting. Contrary to wax, it does not deform during processing or fitting. Burns 100% residue-free, leaves no residue. Does not clog cutters.
Colour :
- transparent.
Package:
1 piece.
...
Kerox- zirconium disc HT 98x12 mm Promotion
Kerox Dental zirconium blocks are made of Yttria material with a perfectly stabilized structure, manufactured by the Japanese industry leader.
Chemical properties:
- composition:
- ZrO2> 94.2%
- Y2O3 - 5.20%
- Al2O3 - 0.25%
- HfO2 <0.30%
- SiO2 <0.02%
- Fe2O3 <0.01%
- Na2O <0.04% Physical properties
- properties after sintering:
- Density (g / cm3) - 6.05
- Bending strength (MPa) - 1500
- Hardness (HV10) - 1250
- Radioactivity (Bq / g) - <0.01
Highly translucent Kerox Dental blocks with exceptional light transmission and high strength at the same time. Compared to standard zirconium, they transmit 25% more light, ensuring the best possible, natural aesthetic effect expected by patients.
Advantages:
Extraordinary aesthetic parameters Highest level
...Kerox- zirconium disc HTML 98x20mm
Characteristics :
Kerox - HT Myltilayer zirconium disc
Features: & nbsp & nbsp multi-layer zirconium disc with high translucency. & nbsp & nbsp 6 layers of natural gradient from neck to incisal & nbsp & nbsp high translucency for natural aesthetics & nbsp & nbsp high mechanical strength & nbsp & nbsp perfect contraction & nbsp & nbsp compatible with most Cad / Cam systems
Application: & nbsp & nbsp full-contour crowns
692.59zł +vat