Product Code:: 260
Remanium GM 380+ Promotion
Dentaurum

6.20zł +vat

6.70zł incl tax

Remanium GM 380+ Promotion

Remanium GM 380 + for standard high-strength structures. Universal use in the technique of skeletal dentures.

Features:

  • Every 64.6%
  • Cr 29%
  • Mo 4.5%
  • other SI, Mn, N, C.
  • The initial melting temperature of 1300 degrees C.
  • The final melting temperature is 1370 degrees C.

Package:

  • 1 piece.

Product Code: 260
Brand: Dentaurum
Remanium GM 380+ Promotion

6.20zł +vat

6.70zł incl tax

Product Code:: 261
Remanium CS +
Dentaurum

13.75zł +vat15.80zł

14.85zł incl tax

Remanium CS +

Rmanium CS + ceramic alloy does not contain beryllium. Corrosion resistant, does not change in the mouth.

Chemical composition of the alloy:

  • Ni 61.0%
  • Cr 26.0%
  • Mo 11.0%
  • Si 1.5%
  • Fe, Co, Al, Ce <1.0

Technical data:

  • Yield strength Rp0.2 - 340 MPa.
  • Tensile strength Rm - 580 MPa.
  • Hardness HV 10 - 195.
  • Total elongation after rupture A5 15%
  • Young's modulus (modulus of elasticity) - 170,000 MPa.
  • Density - 8.2 g / cm3.
  • WAK (25- 500 ° C) - 14 x 10 - 6 k - 1.
  • Initial melting point - 1280 ° C.
  • Final melting temperature - 1350 ° C.

Package:

1 piece.

Product Code: 261
Brand: Dentaurum
Remanium CS +

13.75zł +vat15.80zł

14.85zł incl tax

Product Code:: 271
Wironit extrahard
Bego

4.78zł +vat5.50zł

5.17zł incl tax

Wironit extrahard

Wironit extrahard is an ideal alloy for casting elements of combined work.

Features:

  • Composition by weight: Co - 63.0 Cr - 30.0 Mo - 5.0 Si, Mn, C <2.
  • Density 8.2 g / cm3.
  • Melting temperature range 1260-1305 degrees C.
  • Casting temperature 1420 degrees C.
  • Elongation at Break (A5) 4.1%.
  • Tensile strength (Rm) 910 {MPa}.
  • The yield point (Rp 0.2) 625 {MPa}.
  • Modulus of elasticity 225 {GPa}.
  • Hardness acc. To Vickers (HV10) 375.

Package:

1 piece.

Product Code: 271
Brand: Bego
Wironit extrahard

4.78zł +vat5.50zł

5.17zł incl tax

Product Code:: 278
Remanium GM 800+ Promotion
Dentaurum

6.11zł +vat

6.60zł incl tax

Remanium GM 800+ Promotion

Remanium GM 800 + Frame Denture Casting Alloy. The mirror-like luster of the molten metal makes it possible to determine the right moment of casting.

Features:

  • The alloy has a high fracture toughness due to its excellent physical properties.
  • The high modulus of elongated elasticity allows for obtaining delicate, yet stable structures.
  • The reduced hardness facilitates processing and polishing.
  • High surface gloss after electropolishing.
  • Perfect for laser welding.

Chemical composition:

  • Every 63.3%.
  • Cr 30.0%.
  • Mo 5.0%.
  • Si 1%.
  • MN, C, N.

Parameters:

  • Yield strength Rp 0.2 - 720 MPa.
  • Tensile strength Rm - 960 MPa.
  • Hardness HV 10 - 370.
  • Total elongation after rupture A5 - 6.0%.
  • Young's modulus - modulus of longitudinal elasticity - 230,000 MPa.
  • Density - 8.2 g / cm3.
  • Temp. initial melting - 1240 degrees C.
  • Temp. final melting - 1410 degrees C.

Package:

1 piece.

Product Code: 278
Brand: Dentaurum
Remanium GM 800+ Promotion

6.11zł +vat

6.60zł incl tax

Product Code:: 318
Wiron 99
Bego

9.83zł +vat11.30zł

10.62zł incl tax

Wiron 99

Wiron 99 non-precious alloy for firing ceramics or for veneering with plastics.

Features:

  • Beryllium free Extremely corrosion resistant.
  • High strength in any span.
  • High modulus of elasticity.

Percentage by weight:

  • Ni 65.0
  • Cr 22.5
  • Mo 9.5
  • Nb, Si, Ce <0.02

Alloy Characteristics:

  • Silver color.
  • Density - 8.2 g / cm3.
  • Melting temperature range - 1250-1310 C.
  • Pouring temperature approx. - 1450 C.
  • Expansion coefficients in {10- 6K-1}.
  • 25-600 C - 14.0.
  • 25-500 C - 13.8.
  • Elongation at Break (A5) - 25%
  • The yield point (Rp 0.2) - 330 {MPa}
  • Tensile strength (RM) {MPa} - 650.
  • Modulus of elasticity approx. - 205.
  • Hardness acc. Vickers (HV 10) after firing - 180.

Package:

1 piece.

Product Code: 318
Brand: Bego
Wiron 99

9.83zł +vat11.30zł

10.62zł incl tax

Product Code:: 541
Remanium CSe 1 cube Promotion
Dentaurum

6.39zł +vat

6.90zł incl tax

Remanium CSe 1 cube Promotion

Remanium CSe an alloy of the latest generation for ceramics in the crown and bridge technique.

Features:

  • Very good ceramic adhesion, even after several firings.
  • Does not contain beryllium, biocompatible.
  • Mouth corrosion resistant.

Chemical composition:

  • Nothing 61%.
  • Cr 26%.
  • Mo 11%.
  • Si 1.5%.
  • Co, Fe, Al, Ce <1%.

Technical data:

  • Yield strength Rp0.2 - 340 MPa.
  • Tensile strength Rm - 580 MPa.
  • Hardness HV 10 - 195.
  • Total elongation after rupture A5 - 15%.
  • Yung's modulus (modulus of elasticity) - 170,000 MPa.
  • Density - 8.2 g / cm3.
  • WAK (25- 500 C) 14x10- 6K- 1.
  • Initial melting temperature - 1280 C.
  • Final Melting temperature 1350 C.

Package:

1 piece

Product Code: 541
Brand: Dentaurum
Remanium CSe 1 cube Promotion

6.39zł +vat

6.90zł incl tax

Product Code:: 579
Chrome-nickel-iron steel AN (Ni-Cr-Fe)
Mesa

2.43zł +vat2.80zł

2.63zł incl tax

Chrome-nickel-iron steel AN (Ni-Cr-Fe)

A prosthetic nickel-chromium alloy, non-precious, for casting crowns and bridges with acrylic or composite veneers. Chromium-nickel steel enriched with molybdenum allows the use of all known melting methods. The best results can be achieved by melting the alloy in a casting machine with high or medium frequency current. You can also use an oxy-acetylene torch or an electric arc.

Composition in percent:

  • Ni - 27%.
  • Cr - 22%.
  • Fe - 42%.
  • Si - 4%.
  • Mo - 3%.
  • Others - C, Mn, Cu.

Melting temperature range:

  • 1333 - 1380 C.

Temp. casting:

  • 1420st C.

Package :

1 piece.

Product Code: 579
Brand: Mesa
Chrome-nickel-iron steel AN (Ni-Cr-Fe)

2.43zł +vat2.80zł

2.63zł incl tax

Product Code:: 938
Magnum H75
Mesa

3.83zł +vat4.40zł

4.13zł incl tax

Magnum H75

Magnum H75 steel dental alloy for cobalt-based skeletal dentures.

Features:

  • Every 63%.
  • Cr 29%.
  • Mo 6.5%.
  • other C, Si, Fe, Mn.

Package:

1 piece.

Product Code: 938
Brand: Mesa
Magnum H75

3.83zł +vat4.40zł

4.13zł incl tax

Product Code:: 958
Remanium 2000+
Dentaurum

6.39zł +vat

6.90zł incl tax

Remanium 2000+

Remanium 2000+ alloy has excellent physical properties thanks to its continuous casting process.

Features:

  • Crowns and bridges.
  • Telescopic crowns.
  • Prosthetic restorations on implants.
  • Glued bridges.
  • Secondary elements in skeletal dentures (combined works).
  • The alloy does not require oxidation.

Chemical composition in%:

  • Every 61.
  • Cr 25.
  • Mo 7.
  • In 5.
  • Si 1.5.
  • Mn, N <1%.

Technical data :

  • Yield point Rp 0.2 - 700 MPa.
  • Tensile strength Rm - 900 MPa.
  • Hardness HV 10 - 340.
  • Total elongation after rupture A5 - 7.0%.
  • Young's modulus (coefficient of longitudinal elasticity) - 200,000 MPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 C 14x10- 6K- 1.
  • Initial melting temperature - 1325 degrees C.
  • Final melting temperature - 1415st C.

Package:

1 piece.

Product Code: 958
Brand: Dentaurum
Remanium 2000+

6.39zł +vat

6.90zł incl tax

Product Code:: 1141
Nicor NiCr alloy for the substructures of crowns and bridges veneered with ceramics 500g
Schutz Dental

260.24zł +vat299.00zł

281.06zł incl tax

Nicor NiCr alloy for the substructures of crowns and bridges veneered with ceramics 500g

Nicor-alloy NiCr for ceramic veneered crown and bridge frameworks. The material has very good fluid properties and high thermal stability. Suitable for casting thin layers. Strong bond between metal and ceramics.

Properties:

  • Vickers hardness 280 HV 5

  • 0.2 yield point 550 N / mm2

  • Elongation at break approx. 25%

  • Thermal expansion coefficient (25-600 ° C) 14.1 x 10-6K-1

  • Melting range 1260-1350 ° C

  • Density 8.2 g / cm3

  • Composition: Ni 62%, Cr 26%, Mo 11%.

Package:

  • 500g

Product Code: 1141
Nicor NiCr alloy for the substructures of crowns and bridges veneered with ceramics 500g

260.24zł +vat299.00zł

281.06zł incl tax

Product Code:: 1793
Remanium 2001
Dentaurum

5.74zł +vat6.60zł

6.20zł incl tax

Remanium 2001

Remanium 2001 porcelain alloy. It is especially suitable for melting with an oxygen propane burner. Easily processed, soldered, welded, eroded and milled. Corrosion resistant. Free of nickel, beryllium and iron.

Chemical composition in%:

  • Every 63%
  • Cr 23%
  • Mo 7.3%
  • In 4.3%
  • Si 1.6%
  • Mn, N <1%.

Technical data:

  • Yield point Rp0.2 - 660 MPa.
  • Tensile strength Rm - 850 MPa.
  • HV hardness 10 - 336.
  • Total elongation after rupture A5 - 5.5%.
  • Young's modulus (modulus of elasticity) - 195 GPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 C - 14.2x10- 6K- 1.
  • Initial melting temperature - 1325 degrees C.
  • Final melting temperature - 1415 degrees C.

Package:

1 piece.

Product Code: 1793
Brand: Dentaurum
Remanium 2001

5.74zł +vat6.60zł

6.20zł incl tax

Product Code:: 2260
Biosil F1 cube
Degudent

7.99zł +vat8.90zł

8.63zł incl tax

Biosil F1 cube

Biosil F resilient chrome-cobalt prosthetic alloy for casting of skeletal dentures. Thanks to its exceptional elasticity, it is recommended for the performance of skeletal works with long arms of retention clamps.

Features:

  • Composition: Co - 64.8%, Cr - 28.5%, Mo - 5.3%, Si - 0.5%, Mn - 0.5%, C - 0.4%.
  • Melting point: 1320-1380 ° C.
  • Casting temperature: 1500 ° C.
  • Mold annealing temperature: 1000 ° C.
  • Vickers hardness: 400 HV 10.
  • Tensile strength: 900 N / mm².
  • Destruction limit: 5%.
  • Density: 8.4 g / cm2.
  • Yield point: 700 N / mm².
  • Modulus of elasticity: 220 GPa.

Package:

  • 1 piece.

Product Code: 2260
Brand: Degudent
Biosil F1 cube

7.99zł +vat8.90zł

8.63zł incl tax

Product Code:: 2599
Remanium Star
Dentaurum

9.73zł +vat11.18zł

10.51zł incl tax

Remanium Star

Remanium Star an alloy for ceramics with extremely low hardness. Universal use: crowns and bridges, telescopic crowns, prosthetic restorations on implants, glued bridges, reverse elements in skeletal dentures (combined work).

Chemical composition in%:

  • Every 60.5.
  • Cr 28.
  • In 9.
  • Si 1.5.
  • Mn, N, Nb <1.

Technical data :

  • Yield strength Rp 0.2 - 620 MPa.
  • Tensile strength Rm - 845 MPa.
  • Hardness HV 10 - 280.
  • Total elongation after rupture A5 - 10.2%.
  • Young's modulus (coefficient of longitudinal elasticity) - 190,000 MPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 ° C 14.1x10- 6.
  • Initial melting temperature - 1320 degrees C.
  • Final melting temperature - 1420 degrees C.

Package:

1 piece.

Product Code: 2599
Brand: Dentaurum
Remanium Star

9.73zł +vat11.18zł

10.51zł incl tax

Product Code:: 3388
Gold Ips.D. Sign 96 5g
Ivoclar Vivadent Technical

1,384.26zł +vat

1,495.00zł incl tax

Gold Ips.D. Sign 96 5g

Ips d.Sign 96 High gold-content porcelain alloy Specially developed for metal structures used in conjunction with IPS d.Sign Fluoroapatite Glass Ceramics. It can also be used to make metal structures for IPS Classic and IPS Inline ceramics and others.

Indications:

  • Recommended for making inlays / onlays,
  • partial crowns,
  • total crowns,
  • telescopic and conical crowns,
  • crown-root inlays,
  • bridges with short and long spans.

The percentage composition:

  • Au - 73.8
  • Fri - 8.5
  • Pd - 5.4
  • Ag - 9.0
  • In - 1.9
  • Nb - <1
  • Mn - <
  • Fe - <1
  • Ta - <1
  • Li - <1
  • Ru - <1
  • Re - <1

Technical data:

  • Type - 4
  • Color - yellow
  • Density (g / cmł) - 16.7
  • Melting temperature (° C) - 1050 - 1170
  • Casting temperature (° C) - 1225 - 1285
  • Modulus of elasticity (MPa) - 92.00
  • CTE 25 - 500 ° C - 14.3
  • CTE 20 - 600 ° C - 14.5
  • Elongation (%) - 14.0
  • Hardness on the Vickers scale - 215
  • Yield point (0.2% elongation) (MPa) - 405

Package:

5g

Product Code: 3388
Gold Ips.D. Sign 96 5g

1,384.26zł +vat

1,495.00zł incl tax

Product Code:: 6192
Wirobond 280
Bego

11.68zł +vat13.00zł

12.61zł incl tax

Wirobond 280

Wirobond 280 is a non-noble, top-quality alloy for work in metal ceramics or acrylic veneering, free of nickel and beryllium.

Features:

  • Extremely corrosion-resistant thanks to the optimal interaction of the two basic elements chromium and molybdenum.
  • Low heat conduction.
  • Combines well with ceramics.

Percentage by weight:

  • Co 60.2, Cr 25, W 6.2, Mo 4.8, Ga 2.9, Si, Mn <2

Package:

1 piece.

Product Code: 6192
Brand: Bego
Wirobond 280

11.68zł +vat13.00zł

12.61zł incl tax

Product Code:: 7069
4 all metal for porcealan 250g
Ivoclar Vivadent Technical

328.23zł +vat402.83zł

354.49zł incl tax

4 all metal for porcealan 250g

4 All nickel-chromium alloy for ceramics.

Features:

  • White color
  • Compatible with feldspar and low-fusing ceramics.
  • Easy casting and processing.
  • Reduced hardness.
  • Biocompatibility with tissues.

Indications:

  • Single crowns.
  • Telescopic and conical crowns.
  • Bridges with short and long spans.
  • Crown-root inlays.

Composition:

  • Nothing 61.4%.
  • Cr 25.7%.
  • Mo 11.0%.
  • Si 1.5%.
  • Mn <1.0, Al <1.0%.

Technical data:

  • Density (g / cm3) - 8.4.
  • Melting point range (deg C) - 1260-1350.
  • Coefficient of linear thermal expansion 25-500 (x10-6 / degrees C) - 13.8, 20-600 (x 10-6 / degrees C) - 14.1.
  • Elongation (%) - 12.0.
  • Hardness on the Vickers scale - 235.
  • Yield point (0.2% elongation) (MPa) - 375.

Package:

250g

Product Code: 7069
4 all metal for porcealan 250g

328.23zł +vat402.83zł

354.49zł incl tax

Product Code:: 8277
Starbond CoS 1kg
Scheftner

777.78zł +vat

840.00zł incl tax

Starbond CoS 1kg

Starbond CoS is a cobalt-chrome alloy for crowns and bridges, veneered with ceramics or composites. We use it to make fixed and removable prosthetic restorations. In accordance with the requirements of ISO 22674, this alloy is classified as type 4 category. It does not contain beryllium and nickel.

Metal composition in%:

  • Every 59%
  • Cr 25%
  • In 9.5%
  • Mo 3.5%
  • Si 1%
  • others <1% C, Fe, Mn, N

Technical data :

  • The ductility limit (Rp 0.2) 650 MPa
  • Tensile strength 910 MPa
  • Strain at break 8%
  • Modulus of elasticity 200,000 N / mm2
  • Hardness on the Vickers scale \ u2019a 280- 295 HV 10
  • Density 8.8 g / cmł
  • The fluidity range is 1305 - 1400 ° C
  • Casting temperature 1550 ° C
  • Thermal expansion coefficient 20-600 ° C 14.0 um / m ° C

Package:

1 kg

Product Code: 8277
Brand: Scheftner
Starbond CoS 1kg

777.78zł +vat

840.00zł incl tax

Product Code:: 8665
Diadur DFS Metal Co-Cr for 1 kg frames
Dfs

717.62zł +vat798.99zł

775.02zł incl tax

Diadur DFS Metal Co-Cr for 1 kg frames

Characteristic:

Resilient alloy for skeletons, very well suited for thin plates. Biocompatible.

It pours very well.

!!! order a free sample !!!

Chemical composition:

Co 62.5% Cr 30% Mo 5% Si 1% Mn 1% C 0.5%

Properties:

  • density: 8.2 g / cm3
  • melting range: 1260-1320 C
  • pouring temperature: 1450 C
  • elongation at break: 4.5%

Package:

1 kg

Product Code: 8665
Brand: Dfs
Diadur DFS Metal Co-Cr for 1 kg frames

717.62zł +vat798.99zł

775.02zł incl tax

Product Code:: 8666
DFS Diadur metal Co-Cr for skeletons - cube
Dfs

4.94zł +vat5.50zł

5.33zł incl tax

DFS Diadur metal Co-Cr for skeletons - cube

Resilient alloy for skeletons, very well suited for thin plates. Biocompatible.

It pours very well.

Chemical composition:

Co 62.5% Cr 30% Mo 5% Si 1% Mn 1% C 0.5%

Properties:

  • density: 8.2 g / cm3
  • melting range: 1260-1320 C
  • pouring temperature: 1450 C
  • elongation at break: 4.5%

Package:

1 cube

Product Code: 8666
Brand: Dfs
DFS Diadur metal Co-Cr for skeletons - cube

4.94zł +vat5.50zł

5.33zł incl tax

Product Code:: 8667
DFS Niadur Cr-Ni metal for porcelain 1 kg
Dfs

540.84zł +vat649.00zł

584.10zł incl tax

DFS Niadur Cr-Ni metal for porcelain 1 kg

High-quality metal for both single points and complete jobs. It pours very well.

(metal recommended for working with ceramics: Ivoclar-Vivadent, Vita, Kiss, Hera-Ceram.) below the photo you can download the compatibility table with ceramics available on the Polish market

Chemical composition:

  • Ni 62%
  • Cr 24.5%
  • Mo 10.3%
  • Si 1.7%
  • Fe 1.5%

Features:

  • Density: 8.3 g / cm3
  • Melting range: 1313-1350 C
  • Casting temperature: 1500 C
  • Elongation at Break: 16%
  • (20-600 C) CTE: 14.5 µm / mK

Packaging: 1 kg

Product Code: 8667
Brand: Dfs
DFS Niadur Cr-Ni metal for porcelain 1 kg

540.84zł +vat649.00zł

584.10zł incl tax

Product Code:: 8668
DFS Niadur Cr-Ni metal for porcelain
Dfs

4.42zł +vat5.30zł

4.77zł incl tax

DFS Niadur Cr-Ni metal for porcelain

High-quality metal for both single points and complete jobs. It pours very well.

(metal recommended for working with ceramics: Ivoclar-Vivadent, Vita, Kiss, Hera-Ceram.) - below the photo you can download the compatibility table with ceramics available on the Polish market - order a free sample!

Chemical composition:

Ni 62% Cr 24.5% Mo 10.3% Si 1.7% Fe 1.5%

Density: 8.3g / cm3 Melting range: 1313-1350 C Casting temperature: 1500 C Elongation at break: 16% (20-600 C) CTE: 14.5 um / mK

Package: 1 cube (from 6g)

Product Code: 8668
Brand: Dfs
DFS Niadur Cr-Ni metal for porcelain

4.42zł +vat5.30zł

4.77zł incl tax

Product Code:: 8669
Biodursoft DFS nickel-free metal Co-Cr for porcelain 1kg
Dfs

736.67zł +vat936.00zł

795.60zł incl tax

Biodursoft DFS nickel-free metal Co-Cr for porcelain 1kg

Nickel-free metal for crowns and bridges, very easy to process, perfect for casting single points as well as extensive bridges. Below the photo, you can download a table of compatibility with ceramics available on the Polish market

Chemical composition:

Co 61% Cr 24% W 8% Mo 2.5% Nb 1% Mn 1% Si 1% Fe 1%

Density: 8.6g / cm3 Melting range: 1300-1395 C Casting temperature: 1500 C Elongation at break: 5% (20-600 C) CTE: 14.7 um / mK (20-500 C) CTE: 14.4 um / mK

Packaging: 1 kg

Product Code: 8669
Brand: Dfs
Biodursoft DFS nickel-free metal Co-Cr for porcelain 1kg

736.67zł +vat936.00zł

795.60zł incl tax

Product Code:: 8671
Biodursoft DFS nickel-free Co-Cr metal for porcelain - ankle
Dfs

7.13zł +vat

7.70zł incl tax

Biodursoft DFS nickel-free Co-Cr metal for porcelain - ankle

Nickel-free metal for crowns and bridges, very easy to process, perfect for casting single points as well as extensive bridges. Below the photo, you can download a table of compatibility with ceramics available on the Polish market.

Chemical composition: Co 61% Cr 24% W 8% Mo 2.5% Nb 1% Mn 1% Si 1% Fe 1% order a free sample!

Density: 8.6g / cm3 Melting range: 1300-1395 C Casting temperature: 1500 C Elongation at break: 5% (20-600 C) CTE: 14.7 um / mK (20-500 C) CTE: 14.4 um / mK

Packaging: 1 cube (about 6 g.)

Product Code: 8671
Brand: Dfs
Biodursoft DFS nickel-free Co-Cr metal for porcelain - ankle

7.13zł +vat

7.70zł incl tax

Product Code:: 8841
StarLoy C (Duceralloy C) 1 kg
Degudent

1,184.08zł +vat1,390.00zł

1,278.80zł incl tax

StarLoy C (Duceralloy C) 1 kg

Non-precious alloy, based on cobalt-chrome, for ceramic veneering of crowns and bridges.

Alloy Properties:

  • high corrosion resistance
  • excellent mechanical properties
  • thermal expansion coefficient ideal for all modern ceramics
  • does not require oxidation
  • easy and convenient to process

Composition: Co 59.4%, Cr 24.5%, W 10%, Nb 2%, V 2%, Si 1% Melting point 1270 ° C Casting temperature 1370 ° C Vickers hardness 330HV10

Thermal expansion coefficient:

14.0 x 10-6 K-1 (25 ÷ 500 ° C), 14.3 x 10-6 K-1 (25 ÷ 600 ° C).

Package:

1 kg.

Product Code: 8841
Brand: Degudent
StarLoy C (Duceralloy C) 1 kg

1,184.08zł +vat1,390.00zł

1,278.80zł incl tax

Product Code:: 9507
Biosil F 1 kg
Degudent

1,037.04zł +vat

1,120.00zł incl tax

Biosil F 1 kg

Biosil F resilient chrome-cobalt prosthetic alloy for casting of skeletal dentures. Thanks to its exceptional elasticity, it is recommended for the performance of skeletal works with long arms of retention clamps.

Features:

  • Composition: Co - 64.8%, Cr - 28.5%, Mo - 5.3%, Si - 0.5%, Mn - 0.5%, C - 0.4%.
  • Melting point: 1320-1380 ° C.
  • Casting temperature: 1500 ° C.
  • Mold annealing temperature: 1000 ° C.
  • Vickers hardness: 400 HV 10.
  • Tensile strength: 900 N / mm².
  • Destruction limit: 5%.
  • Density: 8.4 g / cm2.
  • Yield point: 700 N / mm².
  • Modulus of elasticity: 220 GPa.

Package:

  • 1 kg.

Product Code: 9507
Brand: Degudent
Biosil F 1 kg

1,037.04zł +vat

1,120.00zł incl tax

Product Code:: 9694
Magnum H75 1kg.
Mesa

585.19zł +vat

632.01zł incl tax

Magnum H75 1kg.

Magnum H75 steel dental alloy for cobalt-based skeletal dentures.

Features:

  • Every 63%.
  • Cr 29%.
  • Mo 6.5%.
  • other C, Si, Fe, Mn.

Package:

1 kg.

Product Code: 9694
Brand: Mesa
Magnum H75 1kg.

585.19zł +vat

632.01zł incl tax

Product Code:: 9921
4ALL 1 kg
Ivoclar Vivadent Technical

976.85zł +vat1,241.17zł

1,054.99zł incl tax

4ALL 1 kg

4 All nickel-chromium alloy for ceramics.

Features:

  • White color
  • Compatible with feldspar and low-fusing ceramics.
  • Easy casting and processing.
  • Reduced hardness.
  • Biocompatibility with tissues.

Indications:

  • Single crowns.
  • Telescopic and conical crowns.
  • Bridges with short and long spans.
  • Crown-root inlays.

Composition:

  • Nothing 61.4%.
  • Cr 25.7%.
  • Mo 11.0%.
  • Si 1.5%.
  • Mn <1.0, Al <1.0%.

Technical data:

  • Density (g / cm3) - 8.4.
  • Melting point range (deg C) - 1260-1350.
  • Coefficient of linear thermal expansion 25-500 (x10-6 / degrees C) - 13.8, 20-600 (x 10-6 / degrees C) - 14.1.
  • Elongation (%) - 12.0.
  • Hardness on the Vickers scale - 235.
  • Yield point (0.2% elongation) (MPa) - 375.

Package:

1 kg

Product Code: 9921
4ALL 1 kg

976.85zł +vat1,241.17zł

1,054.99zł incl tax

Product Code:: 9922
Colado CC 1kg
Ivoclar Vivadent Technical

1,855.00zł +vat

2,003.40zł incl tax

Colado CC 1kg

Collado CC is a nickel-free alloy intended for the fabrication of metal frames, for veneering with ceramic material or composite.

Indications:

  • crowns
  • telescopic crowns
  • crown-root inlays
  • bridges
  • extensive restorations and long bridges
  • restorations placed on implants
  • extensive frameworks on implants.

Chemical composition:

  • Co 59.0% Cr 25.5% Mo 5.5% W 5.0% Ga 3.2% Nb, Fe, B less than 1%

Package:

1 kg

Product Code: 9922
Colado CC 1kg

1,855.00zł +vat

2,003.40zł incl tax

Product Code:: 9948
Remanium GM 380 + 1 kg Promotion
Dentaurum

866.67zł +vat

936.00zł incl tax

Remanium GM 380 + 1 kg Promotion

Remanium GM 380 + for standard construction of high strength. Universal use in the technique of skeletal dentures.

Features:

  • Every 64.6%
  • Cr 29%
  • Mo 4.5%
  • other SI, Mn, N, C.
  • The initial melting temperature of 1300 degrees C.
  • The final melting temperature is 1370 degrees C.

Package:

1 kg

Product Code: 9948
Brand: Dentaurum
Remanium GM 380 + 1 kg Promotion

866.67zł +vat

936.00zł incl tax

Product Code:: 9949
Remanium GM 800 + 1 kg Promotion
Dentaurum

866.67zł +vat

936.00zł incl tax

Remanium GM 800 + 1 kg Promotion

Remanium GM 800 + Frame Denture Casting Alloy. The mirror-like luster of the molten metal makes it possible to determine the right moment of casting.

Features:

  • The alloy has a high fracture toughness due to its excellent physical properties.
  • The high modulus of elongated elasticity allows for obtaining delicate, yet stable structures.
  • The reduced hardness facilitates processing and polishing.
  • High surface gloss after electropolishing.
  • Perfect for laser welding.

Chemical composition:

  • Every 63.3%.
  • Cr 30.0%.
  • Mo 5.0%.
  • Si 1%.
  • MN, C, N.

Parameters:

  • Yield strength Rp 0.2 - 720 MPa.
  • Tensile strength Rm - 960 MPa.
  • Hardness HV 10 - 370.
  • Total elongation after rupture A5 - 6.0%.
  • Young's modulus - modulus of longitudinal elasticity - 230,000 MPa.
  • Density - 8.2 g / cm3.
  • Temp. initial melting - 1240 degrees C.
  • Temp. final melting - 1410 degrees C.

Package:

1 kg

Product Code: 9949
Brand: Dentaurum
Remanium GM 800 + 1 kg Promotion

866.67zł +vat

936.00zł incl tax

Product Code:: 9950
Remanium CSE 1kg Promotion
Dentaurum

888.89zł +vat

960.00zł incl tax

Remanium CSE 1kg Promotion

Remanium CSe an alloy of the latest generation for ceramics in the crown and bridge technique.

Features:

  • Very good ceramic adhesion, even after several firings.
  • Does not contain beryllium, biocompatible.
  • Mouth corrosion resistant.

Chemical composition:

  • Nothing 61%.
  • Cr 26%.
  • Mo 11%.
  • Si 1.5%.
  • Co, Fe, Al, Ce <1%.

Technical data:

  • Yield strength Rp0.2 - 340 MPa.
  • Tensile strength Rm - 580 MPa.
  • Hardness HV 10 - 195.
  • Total elongation after rupture A5 - 15%.
  • Yung's modulus (modulus of elasticity) - 170,000 MPa.
  • Density - 8.2 g / cm3.
  • WAK (25- 500 C) 14x10- 6K- 1.
  • Initial melting temperature - 1280 C.
  • Final Melting temperature 1350 C.

Package:

1 piece

Product Code: 9950
Brand: Dentaurum
Remanium CSE 1kg Promotion

888.89zł +vat

960.00zł incl tax

Product Code:: 10686
Realloy C Nickel-free alloy for ceramics 1 cube
Realloy E.K.

4.44zł +vat

4.80zł incl tax

Realloy C Nickel-free alloy for ceramics 1 cube

Realloy-C

Features:

  • Universal cobalt chrome alloy compatible with all conventional ceramics.
  • High quality
  • Perfect combination with ceramics
  • Cast by all melting methods
  • Easy finish and easy to polish after pouring
  • Also suitable for laser welding
  • Easy removal of oxide after firing the ceramic
  • Biocompatible

Composition:

  • Every 62.5%
  • Cr 24.6%
  • In 8.5%
  • Mo 2.9%
  • Si 1.3%
  • Nb <1% This alloy is nickel and beryllium free and complies with EN ISO 22674, type 4

Technical data:

  • Density 8.3 g / cmł
  • Vickers hardness 285 (HV10)
  • Melting range 1304 - 1369 (° C)
  • Casting temperature 1490 (° C)
  • Recommended combustion temperature 980 (° C)
  • Strength (Rp 0.2) 490 (MPa)
  • Tensile strength (Rm) 920 (MPa)
  • Modulus of elasticity 210 (GPa)
  • Elongation at Break (A5) 10 (%)
  • WAK (25 - 500 ° C) 13.9 (10- 6 K- 1)
  • WAK (25 - 600 ° C) 14.0 (10-6K- 1)

Package:

1 cube

Product Code: 10686
Realloy C Nickel-free alloy for ceramics 1 cube

4.44zł +vat

4.80zł incl tax

Product Code:: 10858
Modelstar S 1kg.-alloy for Co-CR frames
Scheftner

610.56zł +vat

659.40zł incl tax

Modelstar S 1kg.-alloy for Co-CR frames

Resilient base alloy for the fabrication of skeletal dentures with normal clasps and combined work based on cobalt, chromium and molybdenum. According to the requirements of ISO 22674, the alloy is classified as type 5 category. It does not contain beryllium, nickel and cadmium.

** THE PERCENTAGE COMPOSITION:**

  • Every 62.7%
  • Cr 29%
  • Mo 6%
  • other C, Fe, Si <1%

Technical data:

  • The ductility limit (Rp 0.2) - 510-600 MPa
  • Tensile strength - 770-780 MPa
  • Strain at break> 3%
  • Modulus of elasticity - 200-230 GPa
  • Hardness on the Vickers scale - 355 HV 10
  • Connecting with a laser - yes
  • Density - 8.4 g / cm³
  • Liquidity range - 1170 - 1390 ° C
  • Temp. casting - 1490 - 1540 ° C
  • Thermal expansion coefficient - 15-16 μm / m ° C

Package:

  • 1 kg.

Product Code: 10858
Brand: Scheftner
Modelstar S 1kg.-alloy for Co-CR frames

610.56zł +vat

659.40zł incl tax

Product Code:: 10879
Remanium CS + 1kg
Dentaurum

2,466.06zł +vat3,133.35zł

2,663.35zł incl tax

Remanium CS + 1kg

Rmanium CS ceramic alloy does not contain beryllium. Corrosion resistant, does not change in the mouth.

Chemical composition of the alloy:

  • Ni 61.0%
  • Cr 26.0%
  • Mo 11.0%
  • Si 1.5%
  • Fe, Co, Al, Ce <1.0

Technical data:

  • Yield strength Rp0.2 - 340 MPa.
  • Tensile strength Rm - 580 MPa.
  • Hardness HV 10 - 195.
  • Total elongation after rupture A5 15%
  • Young's modulus (modulus of elasticity) - 170,000 MPa.
  • Density - 8.2 g / cm3.
  • WAK (25- 500 ° C) - 14 x 10 - 6 k - 1.
  • Initial melting point - 1280 ° C.
  • Final melting temperature - 1350 ° C.

Package:

1 kg

Product Code: 10879
Brand: Dentaurum
Remanium CS + 1kg

2,466.06zł +vat3,133.35zł

2,663.35zł incl tax

Product Code:: 10880
Remanium 2001 1kg
Dentaurum

736.67zł +vat936.00zł

795.60zł incl tax

Remanium 2001 1kg

Remanium 2001 porcelain alloy. It is especially suitable for melting with an oxygen propane burner. Easily processed, soldered, welded, eroded and milled. Corrosion resistant. Free of nickel, beryllium and iron.

Chemical composition in%:

  • Every 63.
  • Cr 23.
  • Mo 7.3.
  • At 4.3.
  • Si 1.6.
  • Mn, N <1%.

Technical data :

  • Yield point Rp0.2 - 660 MPa.
  • Tensile strength Rm - 850 MPa.
  • HV hardness 10 - 336.
  • Total elongation after rupture A5 - 5.5%.
  • Young's modulus (modulus of elasticity) - 195 GPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 C - 14.2x10- 6K- 1.
  • Initial melting temperature - 1325 degrees C.
  • Final melting temperature - 1415 degrees C.

Package:

1 piece

Product Code: 10880
Brand: Dentaurum
Remanium 2001 1kg

736.67zł +vat936.00zł

795.60zł incl tax

Product Code:: 10881
Remanium 2000 + 1 kg
Dentaurum

736.67zł +vat936.00zł

795.60zł incl tax

Remanium 2000 + 1 kg

Remanium 2000+ alloy has excellent physical properties thanks to its continuous casting process.

Features:

  • Crowns and bridges.
  • Telescopic crowns.
  • Prosthetic restorations on implants.
  • Glued bridges.
  • Secondary elements in skeletal dentures (combined works).
  • The alloy does not require oxidation.

Chemical composition in% - Co 61. - Cr 25. - Mo 7. - W 5. - Si 1.5. - Mn, N <1%.

Technical data :

  • Yield point Rp 0.2 - 700 MPa.
  • Tensile strength Rm - 900 MPa.
  • Hardness HV 10 - 340.
  • Total elongation after rupture A5 - 7.0%.
  • Young's modulus (coefficient of longitudinal elasticity) - 200,000 MPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 C 14x10- 6K- 1.
  • Initial melting temperature - 1325 degrees C.
  • Final melting temperature - 1415st C.

Package:

1 kg

Product Code: 10881
Brand: Dentaurum
Remanium 2000 + 1 kg

736.67zł +vat936.00zł

795.60zł incl tax

Product Code:: 10882
Remanium Star 1kg Promotion
Dentaurum

989.00zł +vat

1,068.12zł incl tax

Remanium Star 1kg Promotion

Remanium Star an alloy for ceramics with extremely low hardness. Universal use: crowns and bridges, telescopic crowns, prosthetic restorations on implants, glued bridges, reverse elements in skeletal dentures (combined work).

Chemical composition in%:

  • Every 60.5.
  • Cr 28.
  • In 9.
  • Si 1.5.
  • Mn, N, Nb <1.

Technical data :

  • Yield strength Rp 0.2 - 620 MPa.
  • Tensile strength Rm - 845 MPa.
  • Hardness HV 10 - 280.
  • Total elongation after rupture A5 - 10.2%.
  • Young's modulus (coefficient of longitudinal elasticity) - 190,000 MPa.
  • Density - 8.6 g / cm3.
  • WAK 25- 500 ° C 14.1x10- 6.
  • Initial melting temperature - 1320 degrees C.
  • Final melting temperature - 1420 degrees C.

Package:

1 kg

Product Code: 10882
Brand: Dentaurum
Remanium Star 1kg Promotion

989.00zł +vat

1,068.12zł incl tax

Product Code:: 10889
Modell EH stop CoCr Realloy 1 cube
Realloy E.K.

4.07zł +vat

4.40zł incl tax

Modell EH stop CoCr Realloy 1 cube

Model EH

CoCr hard casting alloy, ideal for partial dentures

Features:

  • Castable by all melting methods
  • Also suitable for laser welding
  • Corrosion resistant
  • High stability
  • Biocompatible
  • High quality.

Chemical composition:

  • Every 62.5%
  • Cr 30.0%
  • Mo 5.1%
  • Si 1.0%
  • Mn 1.0%
  • C <1%
  • This alloy is nickel and beryllium free and complies with EN ISO 22674, type 5

Technical data:

  • Density 8.2 g / cmł
  • Vickers hardness 375 (HV10)
  • Melting range 1260 - 1320 (° C)
  • Casting temperature 1490 (° C)
  • Yield point (0.2%) 620 (MPa)
  • Tensile strength 920 (MPa)
  • E- module 220 (GPa)
  • Elongation at Break (A5) 4.5 (%)

Package:

1 piece (about 6.17 g)

Product Code: 10889
Modell EH stop CoCr Realloy 1 cube

4.07zł +vat

4.40zł incl tax

Product Code:: 10893
Modell EH alloy CoCr Realloy 1kg for frames
Realloy E.K.

554.63zł +vat

599.00zł incl tax

Modell EH alloy CoCr Realloy 1kg for frames

Model EH

CoCr hard casting alloy, ideal for skeletal dentures

Features:

  • Castable by all melting methods
  • Also suitable for laser welding
  • Corrosion resistant
  • High stability
  • Biocompatible
  • High quality.

Chemical composition:

  • Every 62.5%
  • Cr 30.0%
  • Mo 5.1%
  • Si 1.0%
  • Mn 1.0%
  • C <1%
  • This alloy is nickel and beryllium free and complies with EN ISO 22674, type 5

Technical data:

  • Density 8.2 g / cmł
  • Vickers hardness 375 (HV10)
  • Melting range 1260 - 1320 (° C)
  • Casting temperature 1490 (° C)
  • Yield point (0.2%) 620 (MPa)
  • Tensile strength 920 (MPa)
  • E- module 220 (GPa)
  • Elongation at Break (A5) 4.5 (%)

Package:

1 kg

Product Code: 10893
Modell EH alloy CoCr Realloy 1kg for frames

554.63zł +vat

599.00zł incl tax

Product Code:: 11230
StarLoy C (Duceralloy C) 1 cube (about 8.5 g)
Degudent

11.24zł +vat13.20zł

12.14zł incl tax

StarLoy C (Duceralloy C) 1 cube (about 8.5 g)

Characteristic:

Non-precious alloy, based on cobalt-chrome, for ceramic veneering of crowns and bridges.

Alloy Properties:

  • high corrosion resistance
  • excellent mechanical properties
  • thermal expansion coefficient ideal for all modern ceramics
  • does not require oxidation
  • easy and convenient to process

Technical data:

  • Composition: Co 59.4%, Cr 24.5%, W 10%, Nb 2%, V 2%, Si 1%
  • Melting point 1270 ° C
  • Casting temperature 1370 ° C
  • Vickers hardness 330HV10

- Thermal expansion coefficient:

  • 14.0 x 10- 6 K- 1 (25 ÷ 500 ° C),
  • 14.3 x 10- 6 K- 1 (25 ÷ 600 ° C).

Package:

1 piece.

Product Code: 11230
Brand: Degudent
StarLoy C (Duceralloy C) 1 cube (about 8.5 g)

11.24zł +vat13.20zł

12.14zł incl tax

Product Code:: 11846
Wiron Light 1 pc
Bego

5.74zł +vat

6.20zł incl tax

Wiron Light 1 pc

WironLight - NiCr alloy for veneering ceramics with a conventional thermal expansion coefficient.

The percentage composition:

  • Ni 64.6;
  • Cr 22.0;
  • Mo 10.0; Si 2.1;
  • Nb, Mn, B <1.0.

Benefits :

  • For all those who appreciate high-quality materials and affordable prices. The alloy has a reduced casting temperature (only to 1350 ° C) and a soaking temperature reduced to 800 ° C.

  • This has a positive effect on reducing the reaction of the metal with the investment material, and thus the surface of the cast object is very smooth. This helps to reduce the amount of work involved in machining.

  • Thanks to the excellent strength parameters, it is possible to perform very delicate works, which at the same time will guarantee high safety.

  • The formed oxides on the surface of Wiron light are definitely lighter compared to Ni-Cr alloys from other manufacturers and can therefore be removed more easily and faster.

  • It is an alloy that can be melted both in induction-vacuum foundries and with the use of a torch. Wiron light is also characterized by very good combination values with ceramics from different manufacturers.

Package:

  • 1pc / about 6g

Product Code: 11846
Brand: Bego
Wiron Light 1 pc

5.74zł +vat

6.20zł incl tax

Product Code:: 12161
Starbond CoS 1 pc
Scheftner

6.37zł +vat7.10zł

6.88zł incl tax

Starbond CoS 1 pc

Starbond CoS is a cobalt-chrome alloy for crowns and bridges, veneered with ceramics or composites. We use it to make fixed and removable prosthetic restorations. In accordance with the requirements of ISO 22674, this alloy is classified as type 4 category. It does not contain beryllium and nickel.

Metal composition:

  • Every 59%
  • Cr 25%
  • In 9.5%
  • Mo 3.5%
  • Si 1%
  • others <1% C, Fe, Mn, N

Technical data:

  • The ductility limit (Rp 0.2) 650 MPa
  • Tensile strength 910 MPa
  • Strain at break 8%
  • Modulus of elasticity 200,000 N / mm2
  • Hardness on the Vickers scale \ u2019a 280- 295 HV 10
  • Density 8.8 g / cmł
  • The fluidity range is 1305 - 1400 ° C
  • Casting temperature 1550 ° C
  • Thermal expansion coefficient 20-600 ° C 14.0 um / m ° C

Package:

1 piece

Product Code: 12161
Brand: Scheftner
Starbond CoS 1 pc

6.37zł +vat7.10zł

6.88zł incl tax

Product Code:: 12225
Colado CC 250 g
Ivoclar Vivadent Technical

569.08zł +vat723.07zł

614.61zł incl tax

Colado CC 250 g

Colado CC is a nickel-free alloy intended for metal frameworks, for veneering with ceramic or composite materials.

** Indications: * 8

  • crowns
  • telescopic crowns
  • crown-root inlays
  • bridges
  • extensive restorations and long bridges
  • restorations placed on implants
  • extensive frameworks on implants.

Chemical composition:

  • Every 59.0%
  • Cr 25.5%
  • Mo 5.5%
  • In 5.0%
  • Ga 3.2%
  • Nb, Fe, B less than 1%

Package:

  • 250g

Product Code: 12225
Colado CC 250 g

569.08zł +vat723.07zł

614.61zł incl tax

Product Code:: 12493
Mogucera C - crown alloy 1kg
Scheftner

638.89zł +vat

690.00zł incl tax

Mogucera C - crown alloy 1kg

Non-precious alloy for porcelain casting based on cobalt, chromium and molybdenum, used for the production of permanent and temporary crowns. MoguCera C is free of beryllium, cadmium and nickel.

** THE PERCENTAGE COMPOSITION:**

  • Every 65.0%
  • Cr 28.0%
  • Mo 5.0%
  • Mn 1.0%
  • other components <1% C, Si

Technical parameters:

  • The yield point is 508 MPa
  • Tensile strength - 795 MPa
  • Elongation at Break - 9%
  • Modulus of elasticity - 209 GPa
  • Hardness on the Vickers scale - 300 HV
  • Laser connection - Yes
  • Density - 8.3 g / cm³
  • Liquidity range - 1370 - 1435 ° C
  • Temp. casting - 1535 - 1590 ° C
  • Thermal expansion coefficient (600 * C) - 14.1 μm / m ° C

Package:

  • 1 kg

Product Code: 12493
Brand: Scheftner
Mogucera C - crown alloy 1kg

638.89zł +vat

690.00zł incl tax

Product Code:: 14388
Realloy N + CrNi alloy for ceramics 1 cube
Realloy E.K.

3.15zł +vat

3.40zł incl tax

Realloy N + CrNi alloy for ceramics 1 cube

Realloy-N +

Universal chrome-nickel alloy compatible with all conventional ceramics

Features:

  • Also suitable for laser welding
  • Easy finish after casting
  • Perfect bond with ceramics
  • High quality
  • Biocompatible

Composition:

  • Ni 62.4%
  • Cr 25%
  • Mo 11%
  • Si 1.6% This alloy is beryllium free and complies with EN ISO 22674, Type3

Technical data:

  • Vickers hardness 200 (HV10)
  • Melting range 1280 - 1350 (° C)
  • Casting temperature 1450 (° C)
  • Recommended combustion temperature 980 (° C)
  • Strength (Rp 0.2) 375 (MPa)
  • Tensile strength (Rm) 660 (MPa)
  • Modulus of elasticity 200 (GPa)
  • Elongation at Break (A5) 10.0 (%)
  • WAK (25 - 500 ° C) 13.9 (10- 6 K- 1)
  • WAK (25 - 600 ° C) 14.1 (10-6K- 1)

Package:

1 cube

Product Code: 14388
Realloy N + CrNi alloy for ceramics 1 cube

3.15zł +vat

3.40zł incl tax

Product Code:: 14389
Realloy N + CrNi alloy for ceramics 1 kg
Realloy E.K.

332.59zł +vat449.00zł

359.20zł incl tax

Realloy N + CrNi alloy for ceramics 1 kg

Realloy-N +

Universal chrome-nickel alloy compatible with all conventional ceramics

Features:

  • Also suitable for laser welding
  • Easy finish after casting
  • Perfect bond with ceramics
  • High quality
  • Biocompatible

Composition:

  • Ni 62.4%
  • Cr 25%
  • Mo 11%
  • Si 1.6% This alloy is beryllium free and complies with EN ISO 22674, Type3

Technical data:

  • Vickers hardness 200 (HV10)
  • Melting range 1280 - 1350 (° C)
  • Casting temperature 1450 (° C)
  • Recommended combustion temperature 980 (° C)
  • Strength (Rp 0.2) 375 (MPa)
  • Tensile strength (Rm) 660 (MPa)
  • Modulus of elasticity 200 (GPa)
  • Elongation at Break (A5) 10.0 (%)
  • WAK (25 - 500 ° C) 13.9 (10- 6 K- 1)
  • WAK (25 - 600 ° C) 14.1 (10-6K- 1)

Package:

1 kg.

Product Code: 14389
Realloy N + CrNi alloy for ceramics 1 kg

332.59zł +vat449.00zł

359.20zł incl tax

Product Code:: 14390
Realloy C Nickel-free ceramic alloy 1 kg
Realloy E.K.

554.63zł +vat

599.00zł incl tax

Realloy C Nickel-free ceramic alloy 1 kg

Realloy-C

Features:

  • Universal cobalt chrome alloy compatible with all conventional ceramics.
  • High quality
  • Perfect combination with ceramics
  • Cast by all melting methods
  • Easy finish and easy to polish after pouring
  • Also suitable for laser welding
  • Easy removal of oxide after firing the ceramic
  • Biocompatible

Composition:

  • Every 62.5%
  • Cr 24.6%
  • In 8.5%
  • Mo 2.9%
  • Si 1.3%
  • Nb <1% This alloy is nickel and beryllium free and complies with EN ISO 22674, type 4

Technical data:

  • Density 8.3 g / cmł
  • Vickers hardness 285 (HV10)
  • Melting range 1304 - 1369 (° C)
  • Casting temperature 1490 (° C)
  • Recommended combustion temperature 980 (° C)
  • Strength (Rp 0.2) 490 (MPa)
  • Tensile strength (Rm) 920 (MPa)
  • Modulus of elasticity 210 (GPa)
  • Elongation at Break (A5) 10 (%)
  • WAK (25 - 500 ° C) 13.9 (10- 6 K- 1)
  • WAK (25 - 600 ° C) 14.0 (10-6K- 1)

Package:

1 kg

Product Code: 14390
Realloy C Nickel-free ceramic alloy 1 kg

554.63zł +vat

599.00zł incl tax

Product Code:: 15708
Wironit Co-Cr 1kg
Bego

688.89zł +vat

744.00zł incl tax

Wironit Co-Cr 1kg

Classic alloy for skeletal dentures based on cobalt and chromium (nickel free)

Chemical composition:

  • Every 64,
  • Cr 28.6,
  • Mo 5.0,
  • Si 1,
  • Mn, C <1.

Alloy Characteristics:

  • density 8.2 g / cm3

  • melting temperature range 1260-1305 ˚C

  • casting temperature 1460 ˚C

  • elongation at break (A5) 10%

  • tensile strength (Rm) 880 {MPa}

  • yield point (Rp 0.2) 615 {MPa}

  • modulus of elasticity 225 {GPa}

  • hardness acc. to Vickers (HV10) 360

Product Code: 15708
Brand: Bego
Wironit Co-Cr 1kg

688.89zł +vat

744.00zł incl tax

Product Code:: 15736
Keramit 785 gold - price 1g.
Nobil-Metal

286.11zł +vat

309.00zł incl tax

Keramit 785 gold - price 1g.

A noble alloy, with a high content of gold and platinum, yellow color (compatible with ceramics available on the market), stiff enough for the construction of short and long bridges.

Application:

  • Crowns and bridges.
  • Onlay.
  • Telescopic beams and crowns.

Composition:

  • Au - 78.5%

  • Fri - 9.8%

  • Pd - 7.7%

  • In - 3.7%

Physical properties:

  • Yellow color

  • Density: 17.6 g / cm

  • Melting range: 1110-1230 C

  • Pouring temperature: 1400 ° C

  • Preheating temperature: 800 ° C

  • CET (25-500 C, 25-600 C): 13.9 - 14.1

  • Metal-ceramic adhesion (Schwickerat Crack Initiation Test): 34.38 MPa

  • Modulus of elasticity: 102 GPa

  • Elasticity limit: 510-580 MPa

  • Elongation (fracture): 12-8%

  • Tensile strength: 630-680

  • Vickers hardness HV5 / 30: 220-250-290

Package:

  • according to weight

Product Code: 15736
Keramit 785 gold - price 1g.

286.11zł +vat

309.00zł incl tax

Showing 1 to 49 of 49 (1 Pages)